<div>     I&#39;m working with the beta- SiC, zinc-blend structure, and I have come across some paper talking about the energy formation of a charged defect, e.g. carbon vacancy with positive charge 1, or positive charge 2, or silicon vacancy with positive charge 1 or negative charge 1.  For example, if I&#39;d like to calculate the energy for carbon vacancy with positive charge 2, how would I do that? So would anyone please give me some information on how to make the cell charged in quantum espresso?<br>